Quote:
Originally Posted by LTb1ow
Just a counterpoint, all my stuff at work is 6061 and lives round 200-220* C, never had an issue brought up about yield strengths.
|
I'm not saying it will instantly turn to vanilla pudding if you heat it. Just that if you get it very hot and then bash on it with a hammer you can damage the welded yoke.